AISI 434 Stainless Steel Sheet ASTM A240 434 Stainless Steel 0.4 -
3.0mm SS Sheet
|Products||434 stainless steel sheet||Thickness||0.4 - 3.0mm|
AISI 434 stainless steel is a ferritic stainless steel formulated
for primary forming into wrought products. Cited properties are
appropriate for the annealed condition. 434 is the AISI designation
for this material. S43400 is the UNS number. Additionally, the
British Standard (BS) designation is 434S19.
The graph bars on the material properties cards below compare AISI
434 stainless steel to: wrought ferritic stainless steels (top),
all iron alloys (middle), and the entire database (bottom). A full
bar means this is the highest value in the relevant set. A
half-full bar means it's 50% of the highest, and so on.
chemical composition of grade 434 stainless steel.
Stainless steel SUS434 equal material :
434,AISI 434,S43400,X6CrMo17-1,material 1.4113, 1Cr17Mo, W.Nr. 434
1.SUS434 stainless steel main description:
SUS434 is a ferritic stainless steel.SUS434 stainless steel
containing 12% ~ 30% chromium.Its corrosion resistance, toughness
and weldability with chromium content increases with the increase
of chloride stress corrosion resistance is superior to other types
of stainless steel.
AISI434 Stainless steel mechanical property:
Ensile strength of sigma b (MPa) : p. 450
Conditions to yield strength sigma (0.2 MPa) : p. 205
Elongation delta (%) : p. 22
Reduction of area bits (%) : 60 or higher
Hardness: 183 hb or less
Grade 434 stainless steel can be forged at 1094 -1149°C
(2000-2100°F) after thorough soaking.
Grade 434 stainless steel is annealed by soaking at 788 - 872°C
(1450-1600°F) followed by cooling in air.
Grade 434 stainless steel does not react to heat treatment.
Grade 434 stainless steel is used in automotive trim applications
and other exterior environments.