Strip, Coil, Foil, Wire, ASTM A268, ASTM A240
Food processing, brewery and wine making equipment, hot-water
tanks, heat-exchanger tubing and automotive components
Type 444 is a low carbon, low nitrogen, ferritic stainless steel
that provides pitting and crevice corrosion resistance superior to
most ferritic stainless steels. Applications requiring superior
corrosion resistance and resistance to chloride stress corrosion
cracking are ideal for this alloy.
Carbon: 0.025 max
Manganese: 1.00 max
Nickel: 01.00 max
Molybdenum: 1. 75-2.50
Titanium+ Columbium : 0.20 + 4x (Carbon+ Nitrogen) min-0.80 max
Phosphorus: 0.040 max
Sulfur: 0.030 max
Density: 0.28 lbs/in3 7.75 g/cm3
Electrical Resistivity: microhm-in (microhm-cm):
68 ° F (20 ° C): 22.50 (57)
Specific Heat: BTU/lbl° F (kJ/kg•K):
32 - 212 ° F (0 - 100 ° C): 0.102 (0.427)
Thermal Conductivity: BTU/hr/ft2/ft/° F (W/m•K)
At 212 °F (100 °C): 15.5 (26.8)
Mean Coefficient of Thermal Expansion: in/inl° F (µm/m•K):
32 - 212 ° F (0 - 100 °C): 6.1 x 10-s (11.0)
Modulus of Elasticity: ksi (MPa)
29 x 103 (200 x 103) in tension
Magnetic Permeability: Magnetic
Melting Range: 2700 - 2790 ° F (1482 - 1532 °C)
Coil - Strip, Foil, Ribbon Wire - Profile, Round, Flat, Square
MECHANICAL PROPERTIES AT ROOM TEMPERATURE
Ultimate Tensile Strength: 60 KSI min (414 MPa min)
Yield Strength (0.2% offset): 40 KSI min (276 MPa min)
Elongation: 22% min
Hardness: Rb 90 max
Type 444 can be rolled to various tempers. Consult Ulbrich
Technical Services if temper rolled product is required.
Refer to NACE (National Association of Corrosion Engineers) for
# 1 - Hot rolled annealed and descaled. It is available in strip,
foil and ribbon. It is used for applications where a smooth
decorative finish is not required.
# 2D - Dull finish produced by cold rolling, annealing and
descaling. Used for deep drawn parts and those parts that need to
retain lubricants in the forming process. # 2B - Smooth finish
produced by cold rolling, annealing and descaling. A light cold
rolling pass is added after anneal with polished rolls giving it a
brighter finish than 2D.
#BA- Bright annealed cold rolled and bright annealed
#CBA- Course bright annealed cold rolled matte finish and bright
#2 - Cold Rolled
# 2BA- Smooth finish produced by cold rolling and bright annealing.
A light pass using highly polished rolls produces a glossy finish.
A 2BA finish may be used for lightly formed applications where a
glossy finish is desired in the formed part. Polished - Various
grit finish for specific polish finished requirements.
* Not all finishes are available for all alloys - Contact Ulbrich
Sales for more information.
XC - Extra clean bright annealed or bright annealed and cold rolled
Grease - Ultra-bright finish (for decorative applications) Soap -
Soap is not removed from tempered wire to act as a lubricant.
* Contact Ulbrich Wire for custom wire finishes.
Type 444 provides excellent formability and can be readily deep
drawn and spin formed. Stretch forming, however, is limited in
application for this alloy.
Type 444 is non-heat treatable.